Konstrukční díly

BÖHLER L625 is a non-magnetizable corrosion and heat resistant nickel alloy in the form of bars, forgings and semi-finished products up to max 254 mm diameter/ cross-section and oxidation resistant up to 1093°C. Best fatigue strength and resistance to stress corrosion cracking when exposed to chloride containing media. Good weldability.

BÖHLER N352 is a martensitic chromium steel with nickel addition. Heat treatable grade, capable of taking a mirror finish. Higher corrosion resistance compared to 13% chromium steal. Resistant to the effects of seawater, weak acids and alkaline solutions, as well as to acids having a strong, oxidizing effect such as nitric acid. Surface finish for optimum corrosion resistance: fine ground or polished. For components subject to high mechanical and corrosive stress, e.g. screws and shafts, at operating temperatures up to approx. 752° F.

BÖHLER N360 is a premium aircraft quality corrosion resistant, martensitic stainless steel, produced using the P-ESR-process. Compared to conventionally produced Cr and CrMo steels, BÖHLER N360 offers improved corrosion resistance and toughness properties as well as high hardness and compressive strength. It is typically used for anti-friction bearing components e.g. bearings, ball screws and wear resistant components for use in the aircraft industry and for automotive components, requiring resistance to both corrosion and wear with hardness not lower than 58 HRC after hardening and tempering, but usage is not limited to such applications.

BÖHLER N700 is a high-quality corrosion-resistant steel in aerospace quality, in the form of bars, wire and forgings with a diameter/thickness of up to 203 mm in the solution-annealed condition, as well as starting material of any size for forging purposes. It is a martensitic, precipitation-hardenable chromium-nickel-copper steel with high strength and toughness. Further increases in strength can be achieved by cold forming and subsequent precipitation hardening. These products are typically used for parts requiring corrosion resistance and high strength up to 316°C. However, their use is not limited to such applications. However, use is not limited to such applications. Certain processing methods and operating conditions can cause these products to become susceptible to stress corrosion cracking. For applications such as bolting where stress corrosion cracking is possible, the product should be aged for a minimum of 4 hours at the highest temperature compatible with the strength requirements, but in no case lower than 552°C.

BÖHLER N701 is a high quality, vacuum remelted, corrosion resistant steel for aerospace applications in the form of bars for machining up to 200 mm in diameter. It is a martensitic, precipitation hardenable chromium-nickel-copper steel with high strength and toughness. These products are typically used for parts that require corrosion resistance, high strength up to 600 °F, and exhibit good toughness & strength in the transverse direction of large dimensions. However, use is not limited to such applications. Certain processing methods and operating conditions can cause these products to become susceptible to Stress corrosion cracking.

BÖHLER N701 AMS is a premium, aerospace-quality corrosion-resistant steel available in bars, wire, and forgings with diameters/thicknesses up to 203 mm in the solution-annealed condition, as well as pre-forging stock of any size. It is a martensitic, precipitation-hardenable chromium-nickel-copper steel with high strength and toughness. Further strength increases can be achieved through cold working and subsequent precipitation hardening. These products are typically used for parts requiring corrosion resistance and high strength up to 316 °C and must exhibit good transverse toughness and strength in large dimensions. However, their use is not limited to such applications. Certain processing methods and operating conditions can make these products susceptible to stress corrosion cracking.

BÖHLER N709 is a premium aircraft-quality corrosion-resistant steel in the form of bars, wire, forgings up to 12.0 inches (305 mm) in diameter or least distance between parallel sides in the solution heat treated condition as well as stock of any size for forging. It is a martensitic precipitation hardenable chromium-nickel-molydenum-aluminium steel possessing high strength and toughness. These products have been used typically for parts requiring corrosion resistance, stress-corrosion resistance and high strength up to 600 °F (316 °C) with good ductility and strength in the transverse direction in large section sizes but,but usage is not limited to such applications. Certain processing procedures and service conditions may cause these products to become subject to stress-corrosion cracking.

BÖHLER N717 is a premium quality, corrosion-resistant steel for aerospace applications, supplied in the form of bars, wire, forgings in the solution-annealed condition, and pre-material of any size for forging. It is a martensitic, precipitation-hardenable chromium-nickel-molybdenum-aluminum steel with high strength and toughness. This steel is typically used for components requiring corrosion resistance and a combination of high strength and toughness up to 427 °C, although its use is not limited to such applications. Certain processing methods and service conditions may lead to stress corrosion cracking in these products.

Tento materiál se díky dobré kombinaci vlastností, jako je dobrá tvářitelnost, vysoká pevnost a dobrá odolnost proti korozi, výborně hodí pro široké spektrum aplikací v leteckém a kosmickém průmyslu.

“This specification covers a corrosion and heat resistant steel in the form of bars, wire, forgings and forging stock. It is an austenitic, precipitation hardenable, iron-nickel-chromium-molydenum-titanium steel of ESR quality. Alloying elements of aluminium and titanium allow this material to undergo precipitation hardening (ageing) through the formation of intermetallic phases. The addition of molybdenum increases the mechanical properties and resistance to creep at high temperatures. These products have been typically used for parts in power generation engineering i.e. gas turbines requiring moderate strength up to 704 °C (1300 °F) and oxidation resistance up to 816 °C (1500 °F), but their use is not limited to such applications.”

BÖHLER T552 is a premium aircraft-quality corrosion-resistant chromium-nickel-molydenum steel in the form of bars, wire, forgings and stock for forging. These products have been used typically for parts such as compressor wheels and structural members requiring corrosion resistance and high strength up to 800°F (427 °C), but usage is not limited to such applications.

BÖHLER T670 is a corrosion-resistant steel for aerospace applications in the form of bars, wire, and forgings with diameters/thicknesses up to 305 mm in the solution-annealed condition, as well as pre-forging material of any size. It is a martensitic, precipitation-hardenable chromium-nickel-copper-molybdenum steel with high strength and toughness. BÖHLER T670 is primarily suitable for parts requiring corrosion resistance close to that of Cr-Ni 18-8 steels and exceeding the strength of martensitic 12% Cr steels. This steel can be processed in the solution-annealed condition and, through precipitation treatment, achieves tensile strengths of up to 1080 MPa with good ductility and strength in the transverse directions, even in large cross-sections. Certain processing methods and operating conditions can cause stress corrosion cracking in these products.

BÖHLER V145 is a Cr-Ni-Mo- steel for applications requiring high tensile and toughness values, in particular in large cross sections in the quenched and tempered condition. The molybdenum addition prevents the steel from being susceptible to temper embrittlement. Highly stressed components with large cross sections for aircraft, such as gear shafts and landing gear components.

BÖHLER V250 is a premium aircraft-quality, maraging alloy steel in the form of bars, forgings and stock for forging. In contrast to heat treatable steels its outstanding tensile properties are not due to a hardened structure with relatively high carbon content, but to precipitation of intermetallic phases from a ductile nickel bearing matrix containing almost no carbon.  These products have been used typically for parts requiring through hardening, without quenching, to a minimum yield strength of 247 ksi (1700 MPa) and where such parts may require welding during fabrication, but usage is not limited to such applications. E.g highly stressed components for the aircraft and rocket industries.

BÖHLER V250AMS is a premium aircraft-quality, maraging alloy steel in the form of bars, forgings and stock for forging up through 10 inches (254.00 mm) inclusive in diameter or least distance between parallel sides. In contrast to heat treatable steels its outstanding tensile properties are not due to a hardened structure with relatively high carbon content, but to precipitation of intermetallic phases from a ductile nickel bearing matrix containing almost no carbon.  These products have been used typically for parts requiring through hardening, without quenching, to a minimum yield strength of 240 ksi (1655 MPa) and where such parts may require welding during fabrication, but usage is not limited to such applications. E.g highly stressed components for the aircraft and rocket industries.

BÖHLER V300 covers a premium aircraft-quality, maraging alloy steel in the form of bars, forgings and stock for forging up through 10 inches (254.00 mm) inclusive in diameter or least distance between parallel sides. In contrast to heat treatable steels its outstanding tensile properties are not due to a hardened structure with relatively high carbon content, but to precipitation of intermetallic phases from a ductile nickel bearing matrix containing almost no carbon.  These products have been used typically for parts requiring through hardening, without quenching, to a minimum yield strength of 270 ksi (1862 MPa) and where such parts may require welding during fabrication, but usage is not limited to such applications. E.g highly stressed components for the aircraft and rocket industries.

BÖHLER V354 is an alloyed Cr-Mo-V quenched and tempered steel for high strength and high temperature requirements, good weldability and suitable for nitriding. Insensitive to tempering embrittlement due to Mo content. Mainly for components in the aerospace industry to be welded and nitrided with high quenched and tempered strength, at operating temperatures from -75° C to 500° C.

BÖHLER V361 is a 3% Cr-Mo-V nitriding low-alloy steel of premium aircraft-quality, low-alloy steel offering a tensile strength of up to over 1350MPa in the form of bars, forgings, and forging stock. Due to the optimized production route via VIM-melting and VAR-remelting, the steel offers high impact strength and fatigue limit. It may be nitrided in the heat treated condition to obtain a wear resistant surface. It is used typically for nitrided parts such as bearings, operating under heavy loads and high speeds at moderate temperatures, and requiring highest surface hardness, high core toughness, and less distortion than parts made from case hardening steel, but usage is not limited to such applications.

Highly stressed components for the aircraft and rocket industries. Constructional and tool steel for hot and cold working tools used for long-time service at temperatures up to approx. 450°C. Machine tools, Pressure vessels, Gearwheels (nitrided), Screws, Precision parts, Tools for hydrostatic presses, Cold extrusion tools, Cold heading and embossing tools, Plastic moulds, Die casting tools for aluminium and zinc alloys, Hot pressing tools.