Antikorózne ocele - Precipitačne vytvrditeľné (PH) ocele

BÖHLER N700 is a high-quality corrosion-resistant steel in aerospace quality, in the form of bars, wire and forgings with a diameter/thickness of up to 203 mm in the solution-annealed condition, as well as starting material of any size for forging purposes. It is a martensitic, precipitation-hardenable chromium-nickel-copper steel with high strength and toughness. Further increases in strength can be achieved by cold forming and subsequent precipitation hardening. These products are typically used for parts requiring corrosion resistance and high strength up to 316°C. However, their use is not limited to such applications. However, use is not limited to such applications. Certain processing methods and operating conditions can cause these products to become susceptible to stress corrosion cracking. For applications such as bolting where stress corrosion cracking is possible, the product should be aged for a minimum of 4 hours at the highest temperature compatible with the strength requirements, but in no case lower than 552°C.

Diely pre letecký priemysel, čerpadlá a ventily vysokotlakových systémov, hydraulických pohonov s vysokými nárokmi na odolnosť proti korózii, pevnosť a húževnatosť.

BÖHLER N701 AMS is a premium, aerospace-quality corrosion-resistant steel available in bars, wire, and forgings with diameters/thicknesses up to 203 mm in the solution-annealed condition, as well as pre-forging stock of any size. It is a martensitic, precipitation-hardenable chromium-nickel-copper steel with high strength and toughness. Further strength increases can be achieved through cold working and subsequent precipitation hardening. These products are typically used for parts requiring corrosion resistance and high strength up to 316 °C and must exhibit good transverse toughness and strength in large dimensions. However, their use is not limited to such applications. Certain processing methods and operating conditions can make these products susceptible to stress corrosion cracking.

BÖHLER N709 is a premium aircraft-quality corrosion-resistant steel in the form of bars, wire, forgings up to 12.0 inches (305 mm) in diameter or least distance between parallel sides in the solution heat treated condition as well as stock of any size for forging. It is a martensitic precipitation hardenable chromium-nickel-molydenum-aluminium steel possessing high strength and toughness. These products have been used typically for parts requiring corrosion resistance, stress-corrosion resistance and high strength up to 600 °F (316 °C) with good ductility and strength in the transverse direction in large section sizes but,but usage is not limited to such applications. Certain processing procedures and service conditions may cause these products to become subject to stress-corrosion cracking.

BÖHLER N717 is a premium quality, corrosion-resistant steel for aerospace applications, supplied in the form of bars, wire, forgings in the solution-annealed condition, and pre-material of any size for forging. It is a martensitic, precipitation-hardenable chromium-nickel-molybdenum-aluminum steel with high strength and toughness. This steel is typically used for components requiring corrosion resistance and a combination of high strength and toughness up to 427 °C, although its use is not limited to such applications. Certain processing methods and service conditions may lead to stress corrosion cracking in these products.

Na základe dobrej kombinácie vlastností materiálu, napr.: dobrá tvárniteľnosť, vysoká pevnosť a dobrá odolnosť voči korózii je materiál mimoriadne vhodný pre rôzne aplikácie v leteckom a vesmírnom priemysle.