Alloy C4 / UNS N06455 / 2.4610
Alloy C4 / UNS N06455 / 2.4610– high corrosion resistance
Properties of Alloy C4 / UNS N06455 / 2.4610
Alloy C4 / UNS N06455 / 2.4610 is a low-carbon, austenitic nickel-molybdenum-chromium alloy engineered for exceptional corrosion resistance. It demonstrates:
Key Features:
- Outstanding resistance to pitting, crevice, and stress corrosion cracking
- High stability against intergranular corrosion, even after welding
- Excellent performance in reducing environments, including hot contaminated acids
- Good weldability, typically used in the as-welded condition without post-weld heat treatment strength even under extreme conditions
Applications of Alloy C4 / UNS N06455 / 2.4610
Alloy C4 / UNS N06455 / 2. 4610 is widely used in industries requiring high corrosion resistance under aggressive chemical conditions.
- Chemical processing: heat exchangers, reactors, piping systems
- Environmental engineering: flue gas desulfurization, waste incineration
- Fertilizer and pesticide production
- Acid storage and transport vessels
- Pharmaceutical and petrochemical equipment
- Oil & gas (manifolds, valves, drilling tools and components)
Specification Overview
| Material number | 2.4610 |
| Alloy | C4 |
| EN designation | NiMo16Cr16Ti |
| UNS | N06455 |
| Böhler Grade | L004 |
| Semi-finished products (strip, sheet, pipe, rod) | DIN 17744 / DIN 17752 |
| Forged or rolled components | ASTM B 574 / ASME SB 574 /DIN 17752/ VdTÜV 424 |
| Sheets / strips | ASTM B 575 / ASME SB 575 / DIN 17751 / VdTÜV 424 |
| Pipe / Tube | ASTM B 619 / ASME SB 619 / ASTM B 622 / ASME SB 622/ ASTM B 626 / ASME SB 626 |
Physical Properties:
| Property | Value |
|---|---|
| Material Density | 8.64 g/cm³ |
| Melting Point | 1335 – 1380°C |
| Thermal conductivity (20 °C) | 10.1 W/(m·K) |
| Electrical Resistivity | 1.24 -1.25 Ω·mm²/m |
| Thermal Expansion (20–100 °C) | 10.8 × 10⁻⁶/K |
Mechanical Properties:
Soft Annealed
| Property | Typical Value |
|---|---|
| Tensile Strength Rm | ≥ 700MPa |
| Yield strength (Rp0.2) | ≥ 305MPa |
| Elongation A5 | ≥ 40% |
Typical Chemical Composition:
Element Content (wt. %)
| C | Si | Mn | P | S | Co | Cr |
| ≤ 0.009 | ≤ 0.050 | ≤ 1.00 | ≤ 0.020 | ≤ 0.010 | ≤ 2.00 | 14.00 – 17.50 |
| Fe | Mo | Ni | Ti | |||
| ≤ 3.0 | 14.00 – 17.00 | REM | ≤ 0.70 |
Product Portfolio
Our company offers Alloy C4 / UNS N06455 / 2.4610 in a wide range of forms and processing stages:
- Sheets and Plates – hot/cold rolled, solution annealed
- Bars and Rods – forged or rolled, pickled
- Tubes and Pipes – seamless or welded
- Wire – drawn or rolled
- Fittings and Flanges
- Forged and Machined Components – per drawing or specification
All information without guarantee and for informational purposes only.